MaragingSteel MS1
SLM(Selective Laser Melting)
Through hardening up to 54 HRC
High strength and hardness
Description
Parts built in MaragingSteel MS1 have a chemical composition corresponding to US classification 18Ni300. This kind of steel is characterized by having very good mechanical properties, and being easily heat treatable to obtain ultra high hardness and strength.
Parts built from MaragingSteel MS1 are easily machinable after the building process and can be heat treated to 54 HRC by solution anneal and age-hardening at 490 °C (914 °F) for 6 hours. In both as-built and heat treated states the parts can be machined, spark-eroded, welded, shot-peened, polished and coated if required.
Properties
The chemical composition in compliance with 18Ni300
Ultimate Tensile Strength 2080 MPa
Yield Strength 2000 MPa
Elongation @ Break 4%
Typical Applications
Mechanical engineering parts