Ti6Al4V grade23

Titanium TC4 Grade 23 is a Ti6Al4V alloy with lower amount of oxygen and iron compared to the standard Ti64 alloy. The chemical composition corresponds to ASTM F136 and ASTM F3001. The material is well-known for having excellent mechanical properties: low density with high strength and excellent corrosion resistance.
Compared to Ti64, Ti64ELI has better elongation and toughness, but lower strength. Generally, Ti64ELI alloys are considered to be biocompatible and have low specific weight compared to CoCr alloys.
Parts built with Titanium TC4 Grade 23 powder can be machined, shot peened and polished in as manufactured and heat treated states. Due to the layerwise building method, the parts have a certain anisotropy. Heat treatment is recommended to reduce internal stresses and increase ductility.

The chemical composition in compliance with Ti6Al4V ELI, ASTM F136, ASTM F3001, ASTM F3302
Ultimate Tensile Strength 1050 MPa
Yield Strength 940 MPa
Elongation @ Break 14%

Other industrial applications where low weight in combination with high strength are required.
Parts for medical industry