Ti6Al4V grade5 wire
Suitable for WAAM (Wire Arc Additive Manufacturing)
Low weight with high strength
Excellent corrosion resistance
Higher fatigue resistance
Description
Titanium Ti64 Grade 23 is a Ti6Al4V alloy with lower amount of oxygen and iron compared to the standard Ti64 alloy. The chemical composition corresponds to ASTM F136 and ASTM F3001. The material is well-known for having excellent mechanical properties: low density with high strength and excellent corrosion resistance.
Compared to Ti64, Ti64ELI has better elongation and toughness, but lower strength. Generally, Ti64ELI alloys are considered to be biocompatible and have low specific weight compared to CoCr alloys.
Parts built with Titanium Ti64 Grade 23 powder can be machined, shot peened and polished in as manufactured and heat treated states. Due to the layerwise building method, the parts have a certain anisotropy. Heat treatment is recommended to reduce internal stresses and increase ductility.
Properties
Typical Part Properties (As-deposited)
Ultimate Tensile Strength： 960±40 MPa
Yield Strength ：850±50 MPa
Elongation @ Break ：15±5%
Typical Applications
Other industrial applications where low weight in combination with high strength are required.
Parts for medical industry